Abstract
ABSTRACTThe interface structure and electrical properties of CeO2/Si (111) grown by laser ablation in ultra high vacuum was investigated by high resolution transmission electron microscopy .Auger electron spectroscopy and capacitance-voltage measurement. The deposited film was single crystalline CeO2 as indicated by RHEED and x-ray diffraction observations. However, during the deposition, a reaction between CeO2 and Si occurred at the interface. This reaction resulted in the formation of an oxygen deficient amorphous CeOX layer and a S1O2 layer. Post annealing in oxygen atmosphere caused the disappearance of the amorphous CeOX and the regrowth of crystalline CeO2. The SiO2 thickness was also increased by annealing. The modified structure of CeO2/SiO2/Si showed a higher break down valtage, compared with the as-deposited sample. From these results, a combination of CeO2 and SiO2 can have a great potential for SOI structure.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.