Growth and properties of ZnO nanowires synthesized by a simple hydrothermal method

Abstract

Hexagonal ZnO nanowires were synthesized on pre-seeded silicon (100) substrates by a simple hydrothermal method at a relatively low temperature of 95 °C without any catalyst or template. The pre-seeded layer was produced using the sol–gel spin coating technique with 1 M zinc acetate in ethanol and ethanolamine. The structural properties of the nanowires were characterized by X-ray diffraction (XRD) and scanning electron microscopy (SEM). The XRD pattern indicated that the as-grown ZnO nanowires had the single-phase wurtzite structure, formed along the c-axis. SEM revealed that the nanostructure thin film had wire textures and the synthesis processes importantly influence the final size and shape of the ZnO nanowires. High-resolution transmission electron microscopy (HRTEM) provided further insight into the structure of ZnO nanostructures. The obtained HRTEM image was of the tip of an individual nanowire. The ZnO nanowires highly preferentially grew in the (002) crystal plane. The lattice spacing between adjacent (002) lattice planes was calculated to be 0.52 nm. The optical characteristics of the nanowires were determined from cathodoluminescence (CL) spectra. The CL revealed a fairly high surface state density of ZnO nanowires that grew at reaction concentrations of 0.01–0.25 M.