NiO thin films with varied oxygen contents are grown on Si(100) and c-Al2O3 at a substrate temperature of 300 °C using pulsed dc reactive magnetron sputtering. We characterize the structure and optical properties of NiO changes as functions of the oxygen content. NiO with the cubic structure, single phase, and predominant orientation along (111) is found on both substrates. X-ray diffraction and pole figure analysis further show that NiO on the Si(100) substrate exhibits fiber-textured growth, while twin domain epitaxy was achieved on c-Al2O3, with NiO(111)∥Al2O3(0001) and NiO[11¯0]∥Al2O3[101¯0] or NiO[1¯10]∥Al2O3[21¯1¯0] epitaxial relationship. The oxygen content in NiO films did not have a significant effect on the refractive index, extinction coefficient, and absorption coefficient. This suggests that the optical properties of NiO films remained unaffected by changes in the oxygen content.

Full Text
Paper version not known

Talk to us

Join us for a 30 min session where you can share your feedback and ask us any queries you have

Schedule a call

Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.