Abstract
As the Sn-Se eutectic solidification produces a lamellar structure, formed by SnSe and SnSe2 compound, which are p and n semiconducting type, respectively, the SnSe-SnSe2 in situ composite is a promising material to be used in photovoltaic device manufacturing. In this work, the Sn-Se alloys corresponding to the eutectic composition as well as to SnSe and SnSe2 composition were processed by direction solidification at several solidification rates in a vertical Bridgman-Stockbarger crystal growth unit. The aim of the experiments was to evaluate the eutectic microstructure behavior as a function of directional solidification parameters. The obtained microstructures were analyzed by using X-ray diffraction and scanning electron and optical microscopies. The results obtained show that a very regular and aligned structure formed by the SnSe and SnSe2 solid phase can be achieved. It was found that the presence of imperfections in the eutectic microstructure depends on the growth rate, and mainly, on the alloy homogenization process.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.