Abstract
A new Nd: Lu 0.141Y 0.855VO 4 mixed laser crystal had been successfully grown by the Czochralski method. The reason of the crystal boule appearing additionally yellowish at the bottom was discussed. The X-ray powder diffraction analysis showed that the as-grown mixed crystal possesses the ZrSiO 4 structure. The effective segregation coefficients of Nd 3+ and Lu 3+ ions in the crystal were measured to be about 0.51 and 0.76, respectively. The room temperature fluorescence spectrum of the mixed crystal showed that the FWHM (full-width at half-maximum) of the 1064.9 nm fluorescence band was 5.1 nm, broader than that of Nd: YVO 4. A continuous-wave (CW) laser output was achieved with the Nd: Lu 0.141Y 0.855VO 4 crystal at 1.06 μm using laser diode pumping. The maximum CW output power of 1.7 W was obtained with the pump power of 7.6 W, higher than the 1.38 W achieved with the 0.5 at% Nd: LuVO 4 crystal under the same experimental conditions. All the results above show that the Nd: Lu 0.141Y 0.855VO 4 crystal is a promising laser material.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.