Abstract
Growth and electrochemical properties of single-crystalline vanadium pentoxide (V2O5) nanorod arrays were investigated. Vanadium pentoxide nanorod arrays were grown by electrochemical deposition, surface condensation induced by a pH change and sol electrophoretic deposition. Uniformly sized vanadium oxide nanorods with a length of about 10 µm and diameters of 100 or 200 nm were grown over a large area with near-unidirectional alignment. Transmission electron microscopy (TEM) micrographs and electron diffraction patterns of V2O5 nanorods clearly show the single-crystalline nature of nanorods fabricated via all three growth routes with a growth direction of [010]. The growth mechanisms of single-crystal V2O5 nanorods have been discussed. Electrochemical analysis revealed that nanorod array electrodes possess significantly improved storage capacity and charge/discharge rate with approximately 5 times higher applicable current density than those of sol-gel derived films. Furthermore, for a given current density, the nanorod array electrode can intercalate up to 3.5 times higher concentration of Li+ intercalation. The relationships between electrochemical property, nano- and microstructure, and growth mechanisms have been discussed.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.