Abstract

BaTiO 3 /SrTiO 3 artificial lattices were deposited on (La,Sr)CoO 3 coated MgO(100) single crystal substrate by pulsed laser deposition (PLD). The stacking thickness ratio of consisting BTO and STO layers was varied while one of the both consisting layers was maintained at 2 unit cell layer thickness. The stacking periodicity of BTO/STO artificial lattice was, therefore in the range from asymmetric BTO 2 unit cell /STO 32 unit cell to BTO 32 unit cell /STO 2 unit cell structure with a total thickness of 100 nm. As the stacking thickness of the BTO layer increased with a fixed stacking thickness of the STO layer (i.e., 2 unit cell thickness), the lattice distortion of the STO layer increased due to mechanical constraint from the thick BTO layer while the lattice distortion of the BTO layer was relatively unchanged. The lattice distortion (c/a) of the STO layer reached at 1.10 for the stacking periodicity of BTO 32 unit cell /STO 2 unit cell . The multiplayer structure with variable stacking thickness of the STO layer and fixed stacking thickness of the BTO layer exhibited the large variation in the lattice distortion of the BTO layer. The dielectric constant of the BTO/STO artificial lattice decreased with the stacking thickness ratio of the BTO and STO layers. This was attributed to severe lattice distortion of the STO (or BTO) in the multiplayer structure of variable stacking thickness of the BTO (or STO) layer. The dielectric constant of the BTO/STO artificial lattice reached a maximum i.e., 1230 at a stacking periodicity of BTO 2 unit cell /STO 2 unit cell.

Full Text
Paper version not known

Talk to us

Join us for a 30 min session where you can share your feedback and ask us any queries you have

Schedule a call

Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.