Abstract
ABSTRACTWe report the growth and characterizations of 31μm thick GaAs films grown on (100) InP substrates by MBE employing different buffer layer structures during the initial deposition. The buffer layer structures under study are: 1) GaAs layer grown at low temperature; 2) GaAs layer grown at low temperature plus two sets of In0.08Ga0.92As/GaAs strained layer superlattices (SLS) and 3) a transitional compositionally graded InxGal-xAs layer between the InP substrate and the GaAs film. After the buffer layer deposition, the growth was continued by conventionalMBE to a total thickness of 3μm for all samples. From the 77K photoluminescence (PL) measurement, it was found that the sample with SLS layers has the highest PL intensity and the narrowest PL linewidth. Cross-sectional transmission electron microscopy (TEM) studies showed that the SLS is effective in reducing the propagation of threading dislocations and explains the observed superior optical quality from the PL measurement.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have