Abstract
We have grown AlGaN/GaN high electron mobility transistor (HEMT) structures by plasma-assisted molecular beam epitaxy on free-standing n-GaN substrates grown by hydride vapor phase epitaxy. Reflection high energy electron diffraction patterns of the as-loaded wafers exhibit narrow streaks which persist throughout the growth. Atomic force microscopy shows smooth AlGaN surfaces with root-mean-square roughness of 10 Å over a 20×20μm2 area. High resolution x-ray diffractometry indicates that the AlGaN peak is ∼20% narrower than for similar structures grown on SiC. Hall mobilities, electron sheet densities, and sheet resistances were measured on ten 60×60μm2 Hall test patterns defined photolithographically across the surface of the 10×10mm2 sample. Buffer leakage measurements demonstrate that a Be:GaN layer effectively isolates the channel from the conductive substrate. Average sheet resistances and sheet densities were 380Ω∕◻ and 0.94×1013cm−2, respectively. These HEMT structures exhibit room-temperature Hall mobilities in excess of 1900cm2∕Vs. In addition, devices on these structures exhibit excellent pinch-off, low gate leakage, and saturated drain current densities of almost 700 mA/mm. Further details regarding the structural and electrical properties will be described along with device testing.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
More From: Journal of Vacuum Science & Technology B: Microelectronics and Nanometer Structures Processing, Measurement, and Phenomena
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.