Abstract
AbstractNanopowders of Y2O3 pure, doped and codoped by Nd3+, Yb3+ were obtained by sol‐gel method. Solution with ethylene glycol was choosed as the proper solution where crystallites of powder with Nd and Yb dopants had the same size. Finally the one‐phased compounds of Y2O3 doped 0.5 at% Nd and 1, 2 or 4 at% Yb were obtained. Grain growth and their morphology were investigated in various temperature and time of heating. The changes of crystallite sizes and lattice constants in relation to the heating time and temperature for the composition Y2O3 doped 0.5 at% Nd and 2 at% Yb are presented. Y2O3 containing 0,5 at% of Nd exhibits intense luminescence bands centered at 920 nm, 1100 nm and 1360 nm whereas a single band at about 1020 nm appears in samples co‐doped with neodymium and ytterbium. Luminescence spectra recorded did not depend on the sample preparation procedure and size of grains. OH impurity affects critically the relaxation dynamics of luminescent ion in nanopowders. (© 2007 WILEY‐VCH Verlag GmbH & Co. KGaA, Weinheim)
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.