Growth and characterization of L-Glycine thiourea nonlinear optical single crystal for optoelectronic applications

Abstract

l-Glycine thiourea single crystals have been grown by slow evaporation solution growth technique (SEST). The cell parameters were estimated from single crystal X-ray diffraction analysis and it was found that the material crystallized in the orthorhombic symmetry with space group P212121 and the theoretical data were estimated. The powder X-ray analysis proved its crystalline nature without the formation of secondary phases. The presence of functional groups and the nature of bonds appearing in the material were identified by FTIR spectroscopy. Optical constants were estimated by UV–Visible spectrum and the lower cut off wavelength was observed at 200 nm. The scanning electron microscope analysis has been carried out to determine the surface morphology of the grown crystal. Energy dispersive spectrum was done to confirm the composition of elements present in the title material. The second harmonic generation (SHG) efficiency was done by Kurtz powder technique and the conversion efficiency was compared with KDP crystal of the title compound. Third order nonlinear optical susceptibility was measured using z-scan technique and it was found that the crystal has a positive refractive index which is self focusing in nature. The obtained results showed that l-glycine thiourea crystals are potential materials for NLO device fabrication.