Abstract

In this research study, aluminum Nitride (AlN) thin film co-doped with erbium and ytterbium has been deposited on Si (100) substrate by RF magnetron Sputtering. After deposition, the film was annealed at 1100 °C in ambient conditions. It’s structural properties were investigated X-ray diffraction (XRD). Thin films morphology is studied using SEM, and EDX provides the chemical composition information. The photoluminescence property of deposited film was investigated by FS5 spectrofluorometer. XRD result revealed that the film has grown along the c-axis oriented in hexagonal wurtzite structure. SEM Result shows that the average size of the particle is 100 nm. The up-conversion luminescence showed intense green and red emission peaks at 530 nm, 552 nm, and 665 nm due to the transition of Er (2H11/2 → 4I15/2, 4S3/2 → 4I15/2, and 4F9/2 → 4I15/2) with excitation of 984 nm. The excitation wavelength with 483 nm photons produces visible luminescence in the green and red region with 557 and 660 nm due to Erbium.

Talk to us

Join us for a 30 min session where you can share your feedback and ask us any queries you have

Schedule a call

Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.