Abstract
Sustainable green composites were engineered from distillers’ dried grains with solubles (DDGS), a co-product from the corn ethanol industry as a sustainable filler in bioplastic matrices made from a carbon dioxide-derived poly(propylene carbonate) (PPC) and poly(3-hyroxybutyrate-co-3-hydroxyvalerate) (PHBV) blend. The effect of water-washed DDGS (15 and 25 wt %) on the properties of injection-molded green composites from PHBV/PPC blends (60/40) and (40/60) and DDGS without and with peroxide (0.5 phr) has been investigated. From the results, it was noticed that the glass transition temperature (Tg) of the PHBV/PPC (60/40) bioplastic matrix increased by ∼9.6 °C by adding a peroxide cross-linking agent, indicating significant interaction (linkage) between PHBV and PPC polymers in this particular composition ratio, which was supported by SEM analysis as no phase separation was observed between PHBV and PPC. The tensile modulus of PHBV/PPC (60/40) and PHBV/PPC (40/60) blends with peroxide was improved by ∼40.7 and 1.5% after the addition of 25 wt % DDGS, respectively, due to its fibrous flaky structure. The % elongation values at break of the PHBV/PPC (60/40) blend matrices with and without peroxide were drastically improved by 18.5 and 90.7 folds, respectively, as compared to that of brittle pristine PHBV.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.