Abstract
In this work, flexible Cu2-xS films on nylon membranes are prepared by combining a simple hydrothermal synthesis and vacuum filtration followed by hot pressing. The films consist of Cu2S and Cu1.96S two phases with grain sizes from nano to submicron. Doping Se on the S site not only increases the Cu1.96S content in the Cu2-xS to increase carrier concentration but also modifies electronic structure, thereby greatly improves the electrical properties of the Cu2-xS. Specifically, an optimal composite film with a nominal composition of Cu2-xS0.98Se0.02 exhibits a high power factor of ~150.1 μW m-1 K-2 at 300 K, which increases by ~138% compared to that of the pristine Cu2-xS film. Meanwhile, the composite film shows outstanding flexibility (~97.2% of the original electrical conductivity is maintained after 1500 bending cycles with a bending radius of 4 mm). A four-leg flexible thermoelectric (TE) generator assembled with the optimal film generates a maximum power of 329.6 nW (corresponding power density of 1.70 W m-2) at a temperature difference of 31.1 K. This work provides a simple route to the preparation of high TE performance Cu2-xS-based films.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.