Abstract
X-ray diffraction and magnetic using dc and ac methods measurements of the polycrystalline and nanosize REMnO3 (RE = Pr, Nd) powdered samples have been performed. The nanosize manganites were synthesized with a sol-gel method at different (800, 850 and 900 °C) temperatures. The average size of synthesized nanoparticles (from 56 to 89 nm) and polycrystalline powders (above 200 nm) was estimated using the x-ray diffraction data. All the compounds studied crystallize in the orthorhombic crystal structure (space group Pnma) at room temperature with smaller values of the lattice parameters in the nanosamples. The temperature-dependent ac magnetic susceptibilities show a sharp high-temperature peak connected with Mn magnetic moments ordering. The low-temperature maximum of magnetic susceptibility is proposed to be due to the polarization of the rare-earth sublattice by an effective exchange field of the Mn ordered sublattice. The antiferromagnetic ordering of Mn sublattice and paramagnetic Curie temperatures as well as the magnetic moment values for the nanosize samples was found to be smaller than those for polycrystalline sample.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.