Abstract
The grain refinement of aluminium alloys is one of the important processes in various industrial fields. This work aims to use aluminium-vanadium (Al-V) master alloy as a new grain refiner for grain refinement of aluminium alloys. The new refiner was prepared by reduction of vanadium pentoxide V2O5 using molten aluminium, then it was examined using SEM, EDS, XRD, and optical microscopy. The findings of these tests indicated that the developed master alloy contains blocky-shaped particles evenly distributed within the aluminium matrix Al3V in the form of an intermetallic compound. Different levels of vanadium content were examined (3.5, 5.6, and 8.3) as grain refiners for commercial pure Al and 6063 alloys. It was found that the grain size was decreased from 2000 to 320 mm for commercial pure aluminium and decreased from 1500 to 300 mm for 6063 alloys. The best results were obtained by using vanadium content of 0.03 wt.% in the refined alloy and a holding time of 3 min. Based on the gross restriction factor (GRF), the new grain refiner Al-V master alloy performed well at vanadium contents more than 0.02 wt.% in the refined alloy.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.