Abstract
Asymmetrical hot rolling (ASHR) was proposed to acquire productive grain refinement for Fe-20Mn-4Al-0.3C and Fe-18Cr-18Mn-0.5N non-magnetic austenitic steels. The intensive additional shear deformation caused by ASHR promotes the nucleation of recrystallization and grain refining of steel plates. With the speed ratio of 1.2, the austenitic grains were refined to ∼5μm on the surface, the recrystallization fraction was enhanced to ∼34.7%, and the thickness of fine-grained surface layer increases to ∼450μm for Fe-20Mn-4Al-0.3C steel. The Fe-18Cr-18Mn-0.5N steel also exhibited an effective surface grain refinement with an average size of ∼3μm, and the recrystallization fraction reached ∼76.9% at the speed ratio of 1.15.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.