Abstract
Grain refinement and superplastic deformation behavior of Zn-Al alloys were investigated in this study. To obtain fine grain size in Zn-0.3Al alloys, rolling and equal channel angular pressing (ECAP) were conducted at temperatures from 40 to 160°C after casting and homogenization heat treatment. Material processing maps for Zn-0.3Al alloy were constructed from a series of compression tests conducted at temperatures from RT to 200°C and strain rates from 3×10-2 to 101 s-1. Superplasticity of ECAPed specimens were evaluated at the temperature of 100°C under the strain rate of 2×10-4 s-1. After ECAP of the Zn-0.3Al alloy, elongation was dramatically increased up to 500%. The effects of ECAP on the texture and anisotropy in the superplastic deformation bebavior were found to be negligible.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.