Abstract
We outline the microstructural, martensitic transformation and magnetic properties of Heusler alloys with starting compositions Ni 50Mn 37Sn 13, Ni 50Mn 36In 14, and Mn 50Ni 40In 10, produced by melt spinning. The ribbons were obtained in argon environment at a high wheel linear speed of 48 m s −1 (typical dimensions: 1.2–2.0 mm in width, 4–12 mm in length, and 7–12 μm in thickness). EDS microanalysis showed that the resulting average elemental chemical composition is slightly shifted with respect to the starting one. Ribbons are fully crystalline and tend to show a highly ordered columnar-like microstructure with grains running through the entire ribbon thickness; the larger dimension of the grains is perpendicular to the ribbon plane. As-spun alloys were single-phase with ferromagnetic bcc L2 1 austenite as high-temperature parent phase. At low temperatures austenite transforms into a structurally modulated martensite with a lattice symmetry that depends on the system (7 M orthorhombic for Ni 50Mn 37Sn 13, 10 M monoclinic for Ni 50Mn 36In 14, and 14 M monoclinic for Mn 50Ni 40In 10). Magnetization isotherms measured in the temperature interval where martensite thermally transforms into austenite confirmed the occurrence of field-induced reverse martensitic transition in the alloys studied.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.