Abstract
Constant-load creep experiments at a temperature of 750 °C and a nominal stress of 300 MPa were conducted on a fine-grained Ti–45Al–5Nb–0.2B–0.2C (in at.%) alloy with a duplex microstructure. Microstructures before and after creep (accumulated strain: 9.6%) were analyzed using scanning and transmission electron microscopy (SEM and TEM). TEM analysis after creep indicates that the individual microstructural constituents of the fine duplex microstructure, namely, the equiaxed γ and the lamellar α 2/γ colonies, undergo varying degrees of deformation and develop various substructures. Lamellar grains deform by dislocation creep. They show clear evidence for dislocation and twin activity. In contrast, only few dislocations are found in the equiaxed grains. We show that the regions with small equiaxed γ grains, representing 65–75 vol.% of the microstructure, deform by grain-boundary sliding.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.