Abstract
High coercivity of hot-deformed Nd2Fe14B magnets was obtained by grain boundary diffusion. Comparable squareness and similar magnetic properties for samples diffusing from side and pole surfaces show little discrepancies if quantities of the infiltrated PrNd-Cu low eutectic alloys is enough to obtain sufficient diffusion. However, the microstructures and higher characteristic peak ratios show preferable orientation of grains near surfaces of the sample diffused from side surfaces than that from pole surfaces. Amorphous Nd-rich phases and crystal Fe-rich phases were both observed in the diffused magnets. The enhancement of coercivity is considered to be resulted from grain boundary optimization and magnetic isolation which is caused by the thickened nonmagnetic intergranular phases.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.