AbstractIt has been shown that acrylic monomer is easily grafted to cellulose by sodium periodate. The apparent activation energy of graft copolymerization is found to be 10.5 Kcal./mole, which indicates that polymer radicals formed by the attack of sodium periodate on cellulose initiate the graft copolymerization. The rate of the reaction increases with increasing reagent concentration of the reagent up to a certain concentration. At higher concentrations, sodium periodate produces more aldehyde groups in the graft copolymer and the grafted chains become shorter. The apparent number of graft‐initiating points is almost constant and independent of the sodium periodate concentration. Studies of homogeneous polymerization indicate that sodium periodate seems not to terminate the reaction of growing polymer radicals. On the other hand, when dialdehyde cellulose prepared previously by sodium periodate oxidation is grafted with methyl methacrylate, the grafted chain is shorter in the range of high content of aldehyde. The above observation indicates that the aldehyde groups formed in cellulose during the grafting reaction are likely to terminate the growing graft chains. The chain transfer constants for several sugars and alcohols with acrylonitrile as monomer were measured. The constants for sugars were found to be always higher than those for alcohols. The x‐ray diffraction patterns of the grafted cellulose with acrylonitrile give, in addition to the typical patterns of crystalline cellulose, lattice distances of 5.2 and about 3 A. which are attributed to the grafted polyacrylonitrile. The intensity distribution curve along the Debye‐Scherrer ring at the lattice distance of 5.2 A. leads to the conclusion that the crystallites of grafted polyacrylonitrile might be oriented along the direction of the fiber axis of the preexisting stock polymer. Studies on samples of cellulose of different fine structure would support the inference that, in the range of relatively low per cent grating the growing grafted chains on the surface of cellulose crystallites are oriented with the formation of crystallites along the lamellar plane of cellulose crystallites.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.