Abstract
A self-forming diffusion barrier (SFB) layer was formed at Cu–Mn/SiO2 interface. Spatial variation of the chemical composition and valence state of the elements in the SFB was investigated in a subnanometer resolution using electron energy loss spectroscopy and transmission electron microscopy. The SFB was found to have a layered structure with graded compositions of nanocrystalline MnO and amorphous MnSiO3. The valence state of Mn was found to be +2 in the MnO layer and gradually increased to +3 in the MnSiO3 layer. The reported dielectric constant of the SFB could be explained by the observed composition and microstructure.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.