Gold Nanostar Characterization by Nanoparticle Tracking Analysis.

Abstract

We demonstrate the application of nanoparticle tracking analysis (NTA) for the quantitative characterization of gold nanostars (GNSs). GNSs were synthesized by the seed-mediated growth method using triblock copolymer (TBP) gold nanoparticles (GNPs). These GNPs (≈ 10 nm) were synthesized from Au3+ (≈ 1 mM) in aqueous F127 (w/v 5%) containing the co-reductant ascorbic acid (≈ 2 mM). The GNS tip-to-core aspect ratio (AR) decreased when higher concentrations of GNPs were added to the growth solution. The AR dependency of GNSs on Au3+/Au(seed) concentration ratio implies that growth is partly under kinetic control. NTA measured GNS sizes, concentrations, and relative scattering intensities. Molar absorption coefficients ∼ 109-1010 M-1 cm-1 (ε400nm) for each batch of GNSs were determined using the combination of extinction spectra and NTA concentrations for heterogeneous samples. NTA in combination with UV-vis was used to derive the linear relationships: (1) hydrodynamic size versus localized surface plasmon peak maxima; (2) ε400nm versus localized surface plasmon peak maxima; (3) ε400nm versus hydrodynamic size. NTA for quantitative characterization of anisotropic nanoparticles could lead to future applications, including heterogeneous colloidal catalysis.