Abstract
Modifying the optical characteristics of rare earth (RE) doped inorganic glasses by stimulating surface plasmon resonance (SPR) via controlled growth of metal nanoparticles (NPs) is an outstanding quest in glass plasmonics. Glasses with composition 70TeO2-20ZnO-10Na2O-(x)Er2O3-(y)Au (x = 0.0 and 1.0 mol%; y = 0.0 and 0.6 mol% both in excess) are synthesized using melt-quenching technique and characterized. Influences of heat treatment temperature on the growth of Au NPs and their subsequent impacts on Raman spectral features modifications are inspected. The amorphous nature of glass is confirmed by using XRD. TEM reveal the non-spherical Au NPs with average diameter vary from 7.4 to 10.3 nm. Surface plasmon band is evidenced around 627 - 632 nm. Raman spectra demonstrate the presence of Er-O and Zn-O bond, anti-symmetric vibrations of Te-O-Te bonds and stretching modes of non-bonded oxygen exists in TeO3 and TeO3+1 unit. The amplifications in Raman signals by a factor of 1.39, 1.40, 0.88 and 1.29 and 1.25 corresponding to the peak centered at 262, 382, 536, 670 and 725 cm-1 are attributed to the contribution of a surface plasmon (SP) generating a strong, localized and secondary field. The excellent features of the results suggest that our systematic method of controlled NPs growth may constitute a basis for improving the spectral features of tellurite glasses useful for the development of efficient and economic up-converted lasers.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.