Global and local investigations of the electrochemical behavior the T6 heat treated Mg–Zn–RE magnesium alloy thixo-cast

Abstract

The influence of semi-solid metal processing (SSM called also as thixoforming) of ZE41A magnesium alloy on the electrochemical behavior in 0.1M NaCl solution was investigated. To describe the corrosion behavior of ZE41A alloy, the electrochemical measurements were conducted in global and local scale for two types of specimens: (1) ingot-feedstock, (2) specimen after thixoforming and T6 treatment. The heat treatment and thixoforming significantly improved mechanical properties of ZE41A alloy. The global corrosion potential is slightly higher for treated sample what is related to the presence of Zr–Zn nanoparticles distributed in solid solution. The corrosion behavior differences between feedstock and thixo-cast after T6 samples are also visible in local scale, what has been revealed by using microcapillary technique. However there is no improvement in corrosion behavior after treatment. Corrosion morphology of the treated sample indicate higher susceptibility to pitting and filiform corrosion. Corrosion rate is also slightly higher.