Abstract
Intergrowth-structured Bi4Ti3O12-BaBi4Ti4O15 (BiT-BBTi) single crystals were grown by a self-flux method, and the crystal structure and polarization properties were investigated. Transmission electron microscope observations and X-ray diffraction analysis presented direct evidence of the intergrowth structure composed of the alternate stacking of BiT and BBTi layers. The BiT-BBTi crystals showed a giant spontaneous polarization (Ps) along the a axis of 52 μC/cm2, which was larger than those of the crystals of BiT (46 μC/cm2) and BBTi (16 μC/cm2). The large Ps of the BiT-BBTi crystals is suggested to originate from the ferroelectric displacements of the Bi of Bi2O2 layers as well as from the Bi substitution for Ba induced by compositional deviation. It was found that the polarization properties of the BiT-BBTi crystals depend strongly on the composition.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.