Abstract

We report results of thermal expansion (TE) and magnetostriction (MS) measurements on a single crystal sample of Gd5(Si0.5Ge0.5)4 prepared by the Bridgman method. TE and MS were measured along the c axis by the strain gauge method and the temperature was controlled using a closed cycle helium refrigerator. From the TE measurements the magnetic structural phase transition temperature was found to be 259.5 K on cooling and 261.5 K on heating. The abrupt change in strain and the temperature hysteresis indicate that it is a first order transition. MS measurements were conducted at 15, 258, and 265 K. At 15 K, the magnetostriction amplitude was 3–4 ppm, whereas at 258 K it was 100 ppm. At 265 K, which is just above the Curie temperature, a giant magnetostriction of 2000 ppm was found. This unusual behavior is due to the fact that the external magnetic field can increase the transition temperature above 265 K, resulting in a first order magnetic/structural phase transition. The results reveal that giant magnetostriction in Gd5(Si0.5Ge0.5)4 only occurs as a result of the magnetic/structural transformation.

Talk to us

Join us for a 30 min session where you can share your feedback and ask us any queries you have

Schedule a call

Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.