Giant electric double-layer capacitance of heavily boron-doped diamond electrode

Abstract

The physical and electrochemical properties of boron-doped polycrystalline diamond electrodes, prepared with various B/C ratio, i.e., 0.1%, 0.5% (BDD-A), 1% (BDD-B), and 5% (BDD-C), were investigated. Electrochemical measurements of the heavily boron-doped films (BDD-C) showed giant electric double-layer capacitance and activity which is significantly larger than BDD-A and BDD-B as well as glassy carbon electrodes. However, interestingly, actual boron concentration of BDD-C was observed to be almost the same as that of BDD-B by secondary ion mass spectroscopy (SIMS) and glow discharge optical emission spectroscopy (GDOES) analysis. It is suggested that the large capacitance is due to a few sp 2-bonded carbon impurities, which was observed only in BDD-C, although the amount of the sp 2-bonded nondiamond species are very small. In the present work, the reason for the interesting electrochemical properties of heavily boron-doped diamond electrodes is discussed. Furthermore, dimensional stability of the electrodes was also confirmed by conducting harsh anodic treatment.