Germanium Nanowire Metal–Oxide–Semiconductor Field-Effect Transistor Fabricated by Complementary-Metal–Oxide–Semiconductor-Compatible Process

Abstract

This work presents a complementary metal-oxide-semiconductor-compatible top-down fabrication of Ge nanowires along with their integration into pMOSFETs with "HfO <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">2</sub> /TaN" high-k/metal gate stacks. Lateral Ge wires down to 14 nm in diameter are achieved using a two-step dry etch process on a high-quality epitaxial Ge layer. To improve the interface quality between the Ge nanowire and the HfO <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">2</sub> , thermally grown GeO <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">2</sub> and epitaxial-Si shells are used as interlayers. Devices with a GeO <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">2</sub> shell demonstrated excellent I <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">ON</sub> /I <sub xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">OFF</sub> ratios (>; 10 <sup xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">6</sup> ), whereas the epitaxial-Si shell was found to improve the field-effect mobility of the holes in Ge nanowires to 254 cm <sup xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">2</sup> V <sup xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">-1</sup> · s <sup xmlns:mml="http://www.w3.org/1998/Math/MathML" xmlns:xlink="http://www.w3.org/1999/xlink">-1</sup> .