Abstract

Glass polyalkenoate cements (GPCs) have potential for skeletal cementation. Unfortunately, commercial GPCs all contain and subsequently release aluminum ions, which have been implicated in degenerative brain disease. The purpose of this research was to create aluminum free GPCs constructed from silicate (SiO2)-calcium (CaO)-zinc (ZnO), glasses mixed with polyacrylic acid (PAA200) in order to evaluate the potential of these novel GPCs for attaching titanium miniplates directly to the skull, a clinical procedure known as cranioplasty. Three glasses were formulated: KBT01 SiO2-CaO-ZnO-sodium (Na2O) glass, KBT02 SiO2-CaO-ZnO-Na2Ogermanium (GeO2), with a 0.03 mol% GeO2 substitution for ZnO and KBT03 SiO2-CaO-ZnONa2O-GeO2, with a 0.06 mol% GeO2 substitution for ZnO in glass structure. X-ray diffraction (XRD) and particle size analysis (PSA) confirmed that all glasses were completely amorphous with similar mean particle sizes. Each glass in the series was mixed with 50 wt% a patented SiO2- CaO-ZnO-strontium (SrO) glass composition, BT101, and subsequently mixed with PAA200 at 50 wt% addition to produce a series of cements. The addition of Ge to the glass series resulted in decreased working times (~142 s to 112 s) and setting times (~807 to 448 s) for the cements manufactured from them. This was due to the increase in crosslink formation during the setting reaction between the Ge-containing glasses and the PAA200. Regarding ion release, Atomic Absorption Spectroscopy (AAS) determined Zn2+ ion release to be 9.56, 8.02 and 5.83 ppm after 30 days for KBT01, KBT02 and KBT03 cements respectively. Germanium ions were not release from the KBT01 cement since the glasses it was formulated from did not contain Ge4+. KBT02 and KBT03 cements released 1.23 ppm and 1.94 ppm of Ge4+ ions after 30 days. The mechanical properties (compressive ~ σc, and biaxial flexural strength ~ σf) of the resulting cements were examined over three time modalities, 1, 7 and 30 days. σc of the cements ranged from ~27- 56 MPa, while σf ranged from ~17-33 MPa. Both strength modalities increased with maturation and increasing Ge content, as Ge may facilitate improved chemical bonding between the COO-groups, thus creating stronger cements in KBT02 and KBT03. The bond strength of the titanium cylinder (Ti) to the bone that it was attached to by the cements increased from ~0.23MPA to 0.63 MPa respectively from placement up to 14 days maturation. Failure of these constructs occurred at the interface between the Ti cylinder and the cement. The results of this research indicate that, due to their novel composition, Ge-based GPCs have suitable handling properties, strengths and adhesiveness for potential in cranioplasty fixation.

Highlights

  • 1.1 Background 1.1.1 Anatomy of the skeleton The human skeleton has 213 bones, not including the sesamoid bones [1]

  • 2.2.4.1 Discussion Shu-Xu et al [66] found that the titanium clamp system offers distinctive advantages compared to suture and stainless steel wire in fractured cranial flap refixation, as no dural separation from bone is necessary for placement

  • This paper aims to investigate the incorporation of Ge and Zn into the Glass polyalkenoate cements (GPCs) glass composition of a KBT glass series (SiO2-calcium oxide (CaO)-ZnO-Na2O) and what effects this will have on the handling and mechanical properties of the resulting GPC

Read more

Summary

Introduction

1.1 Background 1.1.1 Anatomy of the skeleton The human skeleton has 213 bones, not including the sesamoid bones [1]. Bones can be categorized as long, short, irregular and flat bones. Long bones consist of growth plates (epiphysis) at the ends, a shaft (diaphysis), a strong outer surface that is composed of compact (cortical) bone and a spongy inner trabecular (cancellous) bone where the bone marrow is situated. To ensure bone protection and shock absorption, the growth plates of the long bones are sheltered with hyaline cartilage. Short bones include the sesamoid bones, tarsal, patellae and carpal bones. Irregular bones consist of hyoid, coccyx, sacrum, and vertebrae bones [2]. Flat bones include the sternum, scapulae, ribs, mandible and skull [2]. These bones act as a base for muscle attachment and provide important organs with protection. Bone strength is maintained by the modeling and remodeling process bone undergoes, which facilitates adaptation to the changes in biomechanical forces, substituting the micro-damaged old bone with new stronger bone [1]

Objectives
Methods
Results
Conclusion
Full Text
Paper version not known

Talk to us

Join us for a 30 min session where you can share your feedback and ask us any queries you have

Schedule a call

Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.