Abstract
Geopolymer is alumino-silicate material which can apply for many applications due to that geopolymers have several attractive properties of high strength, low permeability, high acid resistance, hazardous materials, and immobilization of toxic materials. This chapter presents synthesis of the dense and the porous structures of geopolymer by using fly ash and industrial waste as the raw materials. Aluminum hydroxide waste (Al-waste) and fly ash (FA) were used to synthesis the dense geopolymers for cement materials. The Al-waste based geopolymer influenced the geopolymer strength, when sodium hydroxide (NaOH) concentration was changed at different curing temperatures. As preliminary microwave oven was exposed in the lower NaOH paste of geopolymer, the successful synthesis of geopolymer cement was obtained. In addition, porous fly ash geopolymers was achieved using a household microwave oven. The geopolymer paste was cured within 1 min by using a microwave oven at different output power. Porous geopolymers were formed immediately as ued at 850 W power of the microwave oven.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.