Abstract
Rice husk and waste glass from sources in Cameroon were used for producing sodium waterglass (NWG) solution denoted S1 and S2 respectively as alternative activators to prepare metakaolin-based geopolymer binder. Metakaolin-based geopolymer binders (G1, G2) were obtained using freshly prepared NWG with a mass ratio NWG/MK=0.83. The IR spectra of S1, S2 using ATR and KBr methods show the presence of SiQ0, SiQ1, SiQ2 units, and S1 contained also SiQ3 and SiQ4 units. The mechanical testing, environmental scanning electron microscopy, mercury intrusion porosimetry, X-ray diffractometry, infrared spectroscopy, amount of binders and thermogravimetric analysis are investigated to study the properties of the geopolymer binders. The results show that the compressive strength values of geopolymer G2 (22.9, 27.6, 32.6, 36 and 39.7MPa) are higher than that of G1 (17.7, 19.1, 21.2, 29.9 and 32.8MPa) at 7, 14, 21, 28 and 56days respectively. The microstructure of G2 is more compact with fewer unreacted metakaolin particles. It can be concluded that sodium waterglass from waste glass and rice husk ash are suitable alternative activators for the production of metakaolin-based geopolymers. In addition, they constitute a better ecological choice when compared to commercial sodium silicate from melting process.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.