Generation of nanocrystalline NiO particles by solution combustion method and its ZnNiO composite coating for corrosion protection

Abstract

AbstractThe nanocrystalline nickel oxide (NiO) particles have been successfully prepared by a simple, fast, economical, and eco‐friendly solution‐combustion method using Ni(NO3)2 · 6H2O (oxidizer) and sugar (dextrose as fuel). The as‐prepared compound was calcined for an hour at different temperatures. The synthesized NiO was characterized by XRD, TGA, SEM/EDX, TEM, XPS, FT‐IR, and UV–Vis spectral methods. The crystallite sizes of the NiO particles were measured. Rietveld refinement of X‐ray data matches the cubic structure with space group of Fm3m (No. 225). The thermal behavior of as‐prepared compound was examined. Scanning electron micrographs show uniform cubic like morphology of NiO and its chemical composition was measured. The TEM results reveal that the particle sizes were in the order of 70–80 nm. The red shift was noticed in UV–Vis absorption spectra. As an application part the ZnNiO composite coating was prepared by electrodeposition method and its corrosion behavior was analyzed by Tafel, impedance and anodic polarization in aggressive medium.