Gelation in free-radical terpolymerization of poly(allyl methacrylate) crosslinked polymer nanosphere with allyl benzoate and vinyl benzoate

Abstract

Microgel-like poly(allyl methacrylate) (PAMA nanosphere) was prepared by the emulsion polymerization of AMA as the reactive crosslinked polymer nanosphere with abundant pendant allyl groups. The terpolymerization of PAMA nanosphere with allyl benzoate (ABz) and vinyl benzoate (VBz) was conducted in bulk using benzoyl peroxide as initiator at 80 °C. The gelation depended on the feed ABz/VBz molar ratio since the molecular weights of resulting poly(ABz-co-VBz)s that act as the bridges increased with an increase in the mole fraction of VBz in the feed monomer. Beyond the gel point, the sol was rapidly incorporated into the gel and the increasing tendency of the gel fraction became steeper from 70 to 95 mol% of VBz as a reflection of increased chain length of bridge between PAMA nanospheres. Moreover, the swelling ratio became lower with increasing the mole percentage of VBz in the feed monomer. These results would support the preferential incorporation of PAMA nanosphere into the gel and the longer bridge can capture more nanospheres to give a much shrunken gel.