Abstract
Abstract The effect of Mg2+ ions on the gel formation in fresh and commercial high ammonia natural rubber latices (FL-latex and commercial HA-latex) was analyzed from the gel content and 2+ content after treatment with (NH4)2SO4. The gel content of rubber from commercial HA-latex decreased significantly after (NH4)2SO4 treatment comparable to that of FL-latex. Long-storage commercial HA-latex containing 50% gel fraction showed no decrease in 2+ content after (NH4)2SO4 treatment. This gel fraction was not solubilized in toluene by the treatment of a proteolytic enzyme in latex or ethanol/toluene mixed solvent extraction of rubber. The 2+ content of rubber in long-storage commercial HA-latex, 0.005% (w/w rubber), decreased after treatment with (NH4)2SO4, while the same treatment showed little change on FL-latex, 0.035%. The toluene soluble fraction of these latices showed a decrease in the Mn value with an increase in the (NH4)2SO4 concentration. The gel content of FL- and HA-lattices increased with an increasing storage period in the presence and absence of (NH4)2SO4. The initial rate of increase in the gel content was slow in the case of FL-latex. These findings indicate that the gel fraction in HA-latex is partly formed by ionic crosslinks caused by 2+ ions. Whereas, the gel phase in long-storage commercial HA-latex is presumed to be a hard gel predominantly formed by covalent bonding.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.