Abstract
Gd0.2Ce0.8O1.9/Y0.16Zr0.84O1.92 (GDC/YSZ) nanocomposite is synthesized by a novel hybrid chemical route, where colloidal crystalline GDC nanoparticles from continuous hydrothermal synthesis are dispersed into a metalorganic YSZ matrix precursor. The result is a mixture of metal oxides in which GDC nanoparticles are finely distributed in a continuous metalorganic polymeric matrix to be crystallized after calcination. The GDC nanoparticles reduce the temperature necessary to obtain crystalline YSZ, which is already formed at 400 °C. The nanocomposite reveals structural stability up to 800 °C when treated in both air and reducing atmosphere, showing the onset of diffusion below 1000 °C. The diffusional processes are largely dependent on the nanometric grain size, with Zr4+ diffusing abruptly towards GDC in air at 1000 °C and GDC/YSZ interdiffusion being hindered in reducing environment despite the onset temperature of 900 °C.The nanocomposite precursor is an inkjet-printable reactive water-based material, suitable for the deposition of thin films with a thickness below 100 nm after calcination at 750 °C. The crystal structure of the film reveals no interaction between GDC and YSZ but a microstrain (0.3% tensile strain for YSZ). The thin film microstructure shows a compact layer with 94% density.The nanocomposite shows high oxygen ionic conductivity at low temperatures (>5⋅10-3 S⋅cm-1 at 500 °C), low activation energy (0.55 eV), and dominant oxygen ionic conductivity even in reducing conditions (pO2 < 10–25 atm). We show that these properties arise from the large interface between the components of the composite, due to the embedding of the GDC nanoparticles in the YSZ matrix, while ZrO-CeO intermixing can be avoided and no n-type conductivity is observed even at low oxygen activities and high temperatures.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.