Abstract
The fabrication of ultrathin oxide films without gas leakage was investigated for the application to low-temperature solid oxide fuel cells (SOFCs). Aluminum thin films were deposited onto two types of anodic nanoporous alumina substrates with pore diameter of 20 and 200 nm, respectively, using dc-magnetron sputter at room temperature. By subsequent oxidation at temperatures over 500 °C, the metal films were successfully transformed into oxide films with thickness of about 35 and 410 nm. Volume expansion induced from oxidation of metal resulted in dense thin films that are free from hydrogen permeation.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.