Abstract
In this study, the effect of the structure of polyether-based polyurethane (PU) membranes on their gas separation properties has been investigated. In this regard, a series of polyurethanes based on hexamethylene diisocyanate (HDI) and 1,4-butanediol as hard segments and different soft segments such as poly(tetramethylene glycol) (PTMG, 2000 g/mol), poly(ethylene glycol) (PEG, 2000 g/mol) and PTMG/PEG mixture were synthesized. PU membranes were prepared by thermal phase inversion method and their physical properties were analyzed by FT-IR, XRD and DSC analyses. The obtained results from FT-IR and DSC analyses indicated that the phase separation of hard and soft segments decreased and chain mobility was restricted, resulting in the increase in glass-transition temperature of the soft segment, by content of the PEG in the PU structure. The permeability of pure N 2 , O 2 , CH 4 and CO 2 gases were determined using constant pressure method at different feed pressures and temperatures. The results of gas permeation experiments showed that by increasing the ether group content in the polymer structure, permeability of the pure gases decreased, while CO 2 /N 2 ideal selectivity increased. The obtained results also indicated that the permeability of CO 2 decrease from 132.52 barrer in PU0 (PU containing 100 wt% of PTMG in soft segment) to 20 barrer in PU100 (the PU containing 100 wt% of PEG in soft segment), respectively. CO 2 /N 2 selectivity increased from 28 to 90. Trade-off evaluation also showed that the potential of studied membranes for commercialization in CO 2 /N 2 and even CO 2 /CH 4 separations increase by PEG content in polymer and the PU membrane which contains 75/25 wt% ratio of PEG/PTMG had the highest. ▸ The effect of soft segment on gas separation properties of PU membrane investigated. ▸ By increasing the amount of PEG in PU, the phase separation decreases. ▸ The solubility domination of gas transport in studied PU membranes investigated. ▸ Low permeability of CO 2 , but high selectivity of CO 2 /N 2, observed for PEG based PU. ▸ The studied PU membranes show high performance in CO 2 /N 2 gas separation.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.