Abstract
GaInNAs/GaAs multiple quantum well (MQW) structures for long wavelength emission were grown by atmospheric pressure metalorganic vapor phase epitaxy using trimethylgallium, trimethylindium, tertiarybutylarsine and dimethylhydrazine precursors. The dependence of the N concentration and the emission wavelength on the In concentration was investigated. The longest wavelengths were obtained with In concentrations of around 23%. Post-growth rapid thermal annealing was performed to enhance the optical quality of the material. Low-temperature photoluminescence (PL) down to 0.77 eV (1.61 μm) was obtained from a Ga 0.74In 0.26N 0.03As 0.97 MQW structure. After annealing the PL wavelength of 1.51 μm was obtained at room temperature.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.