Ga-doped ZnO films deposited with varying sputtering powers and substrate temperatures by pulsed DC magnetron sputtering and their property improvement potentials

Abstract

Ga-doped ZnO (GZO) transparent conductive oxide (TCO) films were deposited on glass substrates by pulsed DC magnetron sputtering with varying sputtering power and substrate temperature while fixing the Ga concentration in the sputtering target. The application of higher sputtering power by pulsed DC magnetrons sputtering at a moderate temperature of 423K results in increased carrier concentration and mobility which accompanied improved doping efficiency and crystalline quality. Substrate temperature was found to be the more dominant parameter in controlling the electrical properties and crystallinity, while the sputtering power played synergistic auxiliary roles. Electrical and optical properties of the GZO TCO films fulfilled requirements for transparent electrodes, despite relatively low substrate temperature (423K) and small thickness (100nm). In an attempt to improve the electrical properties of the GZO films by hydrogen-treatment, it was observed that the substitutional Ga plays the complex role of carrier generator as donor and carrier suppressor deactivating the oxygen vacancy simultaneously, which would complicate the property improvement by increasing doping efficiency.