Abstract
The most recent observations of the response of bulk samples of several commercial solder alloys, exposed to temperatures below the allotropic transition for tin (13C) for extended periods, are reported. Damage associated with tin pest development has been arbitrarily graded into six levels, and the formation of visible a-phase warts used for comparative purposes. Since the previous examination, some 2 years ago, tin pest has been observed for the first time in the traditional Sn-37Pb solder alloy after exposure at 18C and 40C, and actual warts were apparent in as-cast Sn-0.5Cu stored at 40C and in as-cast Sn-3.5Ag after exposure at 18C. No tin pest was detected in Sn-Zn-3Bi after exposure for periods up to 6 years. Tin pest continued to develop in those lead-free alloys in which it had previously been observed, indicating the probability that all would eventually disintegrate in time. In general, prior thermal or mechanical treatment accentuated tin pest formation. The influence of exposure temperature was unclear, since some alloys (Sn-0.5Cu and Sn-3.8Ag-0.7Cu) experienced more damage at 18C, but others (Sn-37Pb and Sn-3.5Ag) were more susceptible at 40C. From a consideration of the findings and other published information, it is contended that impurity levels below 0.1 mass% (1000 ppm) play a vital role in determining whether tin pest develops in realistic timescales. A major factor in the absence of tin pest, to date, on actual joints may be simply the mismatch between the timescales experienced in service and those in long-duration laboratory tests.
Published Version
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.