Abstract
Furfural (F) cannot be easily polymerized like furfuryl alcohol, but it is an aldehyde that can react with urea (U) to make a polymeric network. The possibility of preparing F/U polymer along with an acidic catalyzer (maleic anhydride; M) was evaluated as a means to improve some selected properties of birch (Betula pendula) wood. The F+U/M resin was introduced into the wood with a double treatment technology. The first step involved dilution of F in water and methanol, and the second step was immersion in a U/M aqueous solution. The color of treated wood was darkened after resin curing from brown to a spectrum of black depending on the amount of loaded resin. The 60 to 80% of materials were converted to a non-leachable polymer based on the different formulations. The water absorption and volumetric swelling of the treated samples decreased with an increase in weight percent gain (WPG). The analysis of mechanical strength showed that treatment with F + U/M reduced to some extent the hardness and the impact bending of wood, while modulus of rupture, modulus of elasticity, and compression parallel to the grain with WPG were increased. The exposure of the samples to the accelerated weathering showed noticeable changes in color and roughness.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.