Abstract
Statement of problemThe color of dental poly(methyl methacrylate) (PMMA) is conventionally rendered by organic and inorganic pigments, which are usually not bonded to the polymer network. Functionalized ceramic pigments can be used to color PMMA, allowing improved chemical interaction with the resin matrix. PurposeThe purpose of this in vitro study was to synthesize, functionalize, and characterize pink manganese-doped alumina ceramic pigments. The hypothesis tested was that functionalized ceramic pigments would render pink coloration to a translucent PMMA without jeopardizing its mechanical properties. Material and methodsPink alumina powders doped with 1 or 2 mol% of manganese (Al2O3:Mn) were prepared by means of a polymeric precursor method. Pigment (Pig.) particles were functionalized with a silica coating method followed by silanation before preparation of PMMA-based composite resins (5 wt% pigment). The color of composite resins (Pig.1% and Pig.2%) and PMMA controls (Pink and translucent [Trans]) was evaluated (CIELab color coordinates), and their mechanical properties were tested (3-point bending). ResultsThe microstructure of the pigment particles showed approximately 55-nm nanocrystals of manganese-doped α-alumina clustered into irregular porous particles up to 60 μm. The composite resins and pink PMMA showed similar color parameters (CIE a* pink=20.1, Pig.1%=14.6, Pig.2%=16.0, Trans=0.19, P<.001; CIE b* Pink=17.0, Pig.1%=18.6, Pig.2%=19.0, Trans=2.52, P<.001). No statistical differences were observed in mechanical properties among groups (σf pink=98.4, Pig.1%=98.1, Pig.2%=98.8, trans=89.1, P=.136). ConclusionsThe addition of the functionalized pink ceramic pigments to a translucent PMMA yielded similar coloration to that of the regular pink PMMA used in dentistry and did not jeopardize its mechanical properties.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.