Abstract
Fully dense, doped ZnO varistors were prepared using an easy two‐stage pressureless‐sintering method at temperatures as low as 825°C, with a grain size of ∼0.5 μm. After the highly nonohmic ZnO varistors were sintered, their fine microstructure consisted of uniformly sized grains, small spinel grains with partially dissolved manganese and cobalt oxides discontinuously distributed in the fairly wide grain boundaries, and an intergranular layer of bismuth‐rich crystalline phase mainly detected at three or four ZnO grain junctions. There were twins near the middle of almost all the ZnO grains. The abnormally high nonlinear properties of the almost nanostructured varistors (FB≈ 6–8 kV/mm and α= 270) were attributed to a uniform and very fine microstructure, a high ZnO–ZnO grain direct contacts concentration, and a uniform hybrid layer substructure (grain boundaries and twin boundaries) with different (but probably accumulative) potential barriers.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.