Abstract
Inversion asymmetry in two-dimensional materials grants them fascinating properties such as spin-coupled valley degrees of freedom and piezoelectricity, but at the cost of inversion domain boundaries if the epitaxy of the grown 2D layer -- on a polar substrate -- cannot adequately distinguish what are often near-degenerate 0{\deg} and 180{\deg} orientations. We employ first-principles calculations to identify a method to lift this near-degeneracy: the energetic distinction between eclipsed and staggered configurations during nucleation at a point defect in the substrate. For monolayer MoS2 grown on hexagonal boron nitride, the predicted defect complex can be more stable than common MoS2 point defects because it is both a donor-acceptor pair and a Frenkel pair shared between adjacent layers of a 2D heterostack. Orientation control is verified in experiments that achieve ~90% consistency in the orientation of as-grown triangular MoS2 flakes on hBN, as confirmed by aberration-corrected scanning/transmission electron microscopy. This defect-enhanced orientational epitaxy could provide a general mechanism to break the near-degeneracy of 0/180{\deg} orientations of polar 2D materials on polar substrates, overcoming a long-standing impediment to scalable synthesis of single-crystal 2D semiconductors.
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.