Abstract

Nickel Ferrite ( NiFe2O4) doped with Samarium (Sm) (0.2, 0.3, 0.4, 0.5 mol.%) was prepared by the conventional solid-state reaction. The crystal structure, surface morphology, infrared spectrum of absorption, and magnetic properties of samples were characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM), Fourier transform infrared (FTIR) spectroscopy, and vibrating sample magnetometer (VSM). XRD patterns were indexed with inverse spinel cubic phase with the space group of Fd-3m of nickel ferrite. The average grain size was about 5–10 μm. FTIR spectral study on the NiFe2O4ferrite phase was recorded between 350 cm-1and 4000 cm-1. Two fundamental absorption bands of the ferrites were appeared at 450 cm-1and 1000 cm-1characteristic of metal vibrations. VSM measurements show that the NiFe2O4doped with Sm 0.3% has the highest value of saturation magnetization. It is also easily demagnetized due to the low value of coercivity field it has. Both NiFe2O4doped with Sm 0.2 mol.% and 0.4 mol.% materials have same values of coercivity field. However, NiFe2O4doped with Sm 0.4 mol.% material has the comparatively high value of saturation magnetization than NiFe2O4doped with Sm 0.2%, also this material was hardly demagnetized, and has highest coercivity field.

Full Text
Paper version not known

Talk to us

Join us for a 30 min session where you can share your feedback and ask us any queries you have

Schedule a call

Disclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.