Abstract
The epoxy resin diglycidyl ether of bisphenol F (DGEBF) was cured by the aliphatic amine curing agent Epicure 3371 in a stoichiometric ratio both frontally and in a batch-cure schedule. Glass transition temperatures (Tg) were determined using differential scanning calorimetry (DSC) and dynamic mechanical analysis (DMA). DMA also was used for studying the storage modulus (E*) and tan delta (tan d) of the cured samples. Tensile properties of epoxy samples were tested according to ASTM D638M-93. The properties of the frontally cured epoxy resin were found to be very close to that of batch-cured epoxy resin. Velocity of cure-front propagation was measured for both neat and filled epoxy. Rubber particles (ground tires) were used as a filler. The maximum percentage of filler in the epoxy resin allowing propagation was 30%. Because of convection, only descending fronts would propagate. Advantages and disadvantages of frontal curing of epoxy resins are discussed. q 1997 John Wiley & Sons, Inc. J Appl Polym Sci 66: 1209-1216, 1997
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.