Friction Stir Welding of a Commercial 7075-T6 Aluminum Alloy: Grain Refinement, Thermal Stability and Tensile Properties

Abstract

Commercial 7075-T6 aluminum alloy was subjected to friction stir welding (FSW), resulting in development of a fine-grained structure with average size of about 3 μm in the nugget zone. Static annealing at temperatures ranging from 623 to 773 K for 30 min showed that the fine grain microstructure was stable at temperatures not higher than 723 K. Increase in annealing temperature up to 773 K led to an abnormal grains growth, followed by the development of mm-scale grains. The specimens obtained from the nugget zone demonstrated a superplastic behavior at temperatures ranging from 623 to 723 K and at strain rates ranging from 1 × 10−4 to 1 × 10−2 s−1. Large elongation of about 440% was observed at a temperature of 673 K and at a strain rate of 1 × 10−3 s−1.