Abstract
An initial study was made to evaluate the feasibility of joining magnesium alloy AZ31 sheet to galvanized steel sheet in a lap configuration using friction stir welding (FSW). Two different automotive sheet steels were used for comparative evaluation of the dissimilar joining potential: a 0.8 mm thick, electrogalvanized (EG) mild steel, and a 1.5 mm thick hot-dipped galvanized (HDG) high-strength, low-alloy (HSLA) steel. These steels were joined to 2.33 mm thick AZ31B magnesium sheet. A single FSW tool design was used for both dissimilar welds, and the process parameters were kept the same. The average peak load for the AZ31-1.5 mm steel weld joint in lap shear mode was found to be 6.3 ± 1.0 kN. For the AZ31-0.8 mm steel weld, joint strength was 5.1 ± 1.5 kN. Microstructural investigation indicates melting of the Zn coating present on the steel sheets, and subsequent alloying with the Mg sheet resulted in the formation of a solidified Zn-Mg alloy layer.
Sign-in/Register to access full text options 
Talk to us
Join us for a 30 min session where you can share your feedback and ask us any queries you have
Schedule a callDisclaimer: All third-party content on this website/platform is and will remain the property of their respective owners and is provided on "as is" basis without any warranties, express or implied. Use of third-party content does not indicate any affiliation, sponsorship with or endorsement by them. Any references to third-party content is to identify the corresponding services and shall be considered fair use under The CopyrightLaw.